Título: | Investigação da resistência mecânica e da capacidade de isolamento acústico de compósitos cimentícios leves contendo casca do arroz e palha da planta oryza sativa (arroz) |
Autor(es): | Silva, Débora Bretas |
Primeiro Orientador: | Chong, Wang |
Coorientador: | Marangon, Ederli |
Resumo: | No presente estudo foram analisados um total de dez traços de concreto celular espumoso com adição de fibras vegetais provenientes da planta Oryza Sativa quanto ao seu desempenho mecânico e acústico. Dentre estes, um traço contendo apenas casca de arroz foi tomado como referência, e para os demais foi realizada uma substituição de parte da casca do arroz por palha em três diferentes comprimentos e porcentagens. Para comprovar que se tratavam de compósitos de concreto leve e facilitar futuras reproduções do material, foram aferidas as massas específicas no estado fresco e no estado endurecido aos 28 dias de cura. Na análise mecânica, foram determinadas a resistência à compressão axial e à tração na flexão em três pontos, também aos 28 dias de cura. Em ambos os casos houve um aumento na resistência mecânica em comparação ao traço referência, tornando evidente o benefício da combinação das duas fibras. No que tange a compressão axial verificou-se que o comprimento da palha não influencia o desempenho dos compósitos, além disso, a porcentagem de substituição mais promissora foi a de 5%. Para a tração na flexão em três pontos, o comprimento também foi uma variável que não influenciou os resultados, quanto a porcentagem de substituição, assim como observado no desempenho à compressão 5% foi a quantia que apresentou melhores repercussões no material. Fazendo uma comparação entre os resultados físicos e mecânicos comprovou-se que a densidade não foi um fator determinante para o desempenho mecânico devido a sua pequena variabilidade. A análise acústica foi realizada através de um tubo de impedância, e apesar de os compósitos terem apresentado entre si resultados bem semelhantes devido a não representatividade das amostras, ficou claro que o desempenho acústico é superior em relação a outros materiais habitualmente empregues para a mesma finalidade. |
Abstract: | In the present study, a total of ten traces of foamed cellular concrete with addition of vegetal fibers from the Oryza Sativa plant were analyzed for their mechanical and acoustic performance. Among these, a trace containing only rice husk was taken as reference, and for the others a substitution of part of the rice husk by straw was carried out in three different lengths and percentages. To verify that they were lightweight composites and to facilitate future reproductions of the material, the specific masses were evaluated in the fresh state and in the hardened state at 28 days of cure. In the mechanical analysis, the axial compression strength and the flexural tensile strength were determined at three points also at 28 days of cure. In both cases there was na increase in mechanical resistance compared to the reference trait, making evident the benefit of fiber addition. As far as the axial compression was concerned, it was verified that the straw length did not influence the performance of the composites, in addition the most promising substitution percentage was 5%. For the traction in the three-point flexion the length was also a variable that did not influence the results, as the percentage of substitution, as observed in the compression performance 5% was the amount that presented better repercussions in the material. By comparing the physical and mechanical results it was verified that the density was not a determining factor for the mechanical performance due to its small variability. The acoustic analysis was performed through an impedance tube, and although the composites presented very similar results among themselves due to the non-representativeness of the samples, it was clear that the acoustic performance is superior in relation to other materials commonly used for the same purpose. |
Palavras-chave: | Engenharia civil Fibras vegetais Materiais compósitos Concreto leve Civil engineering Composite materials Lightweight concrete Vegetable fibers |
CNPq: | CNPQ::ENGENHARIAS |
Idioma: | por |
País: | Brasil |
Editor: | Universidade Federal do Pampa |
Sigla da Instituição: | UNIPAMPA |
Campus: | Campus Alegrete |
Citação: | SILVA, Débora Bretas. Investigação da resistência mecânica e da capacidade de isolamento acústico de compósitos cimentícios leves contendo casca do arroz e palha da planta oryza sativa (arroz). 88p. 2017. Trabalho de Conclusão do Curso (Graduação em Engenharia Civil) - Universidade Federal do Pampa, Campus Alegrete, Alegrete, 2017. |
Tipo de Acesso: | Acesso Aberto |
URI: | http://dspace.unipampa.edu.br:8080/jspui/handle/riu/1948 |
Data do documento: | 30-Jun-2017 |
Aparece nas coleções: | Engenharia Civil |
Arquivos associados a este item:
Arquivo | Descrição | Tamanho | Formato | |
---|---|---|---|---|
DÉBORA BRETAS SILVA 2017.pdf | 5.2 MB | Adobe PDF | Visualizar/Abrir |
Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.