Por favor, use este identificador para citar o enlazar este ítem: https://repositorio.unipampa.edu.br/jspui/handle/riu/1691
Tipo: Trabalho de Conclusão de Curso
Título : Análises reológicas no estado fresco e mecânicas de caldas de cimento portland produzidas com aditivos químicos de última geração
Autor(es): Dias Filho, Algacir da Silva
Primeiro Orientador: Venquiaruto, Simone Dornelles
Resumo: Este trabalho tem como objetivo analisar o tempo de vida útil, a compatibilidade, o ponto de saturação e as propriedades mecânicas de três aditivos superplastificantes a base de policarboxilatos em caldas de cimento Portland. Para esse estudo foram confeccionadas caldas com dois tipos de cimento Portland(CP IV e CP IIE) e uma relação de água/cimento de 0,35.Foram analisados os comportamentos das caldas em misturas contendo diferentes teores de aditivo. Os teores eram relacionados com o peso de sólidos dos aditivos pelo peso de cimento, variando de 0,2% a 0,8. Foram realizados ensaios de Funil Marsh e Mini abatimento, onde através da curva de saturação (ponto em que o aditivo deixa de proporcionar melhorias e ocorre um decréscimo de fluidez) pode-se analisar a compatibilidade e o ponto de saturação dos aditivos para cada tipo de cimento. As caldas foram analisadas em diferentes tempos de controle, trinta minutos, uma hora, duas horas, três e quatro horas após a mistura, como objetivo de terminar seu tempo de vida útil(quando o aditivo deixa de exercer melhorias plásticas a calda). As características mecânicas foram determinadas através de ensaios de compressão axial e de tração na flexão na flexão para idades de 7 e 28 dias. Após analises dos resultados observa-se que o ponto de saturação para os três aditivos nas misturas com CP IV ficou entre 0,4% e 0,5%. Para as caldas com cimento CP II E o ponto de saturação ficou entre 0,5% e 0,6%. O Aditivo 03 apresentou melhor compatibilidade e vida útil dentre os aditivos analisados, promovendo ganhos de plasticidade até o último período analisado (quatro horas após a mistura). Nos ensaios de resistência à compressão axial o Aditivo 03 apresentou os melhores resultados para ambas as idades de controle (7 e 28dias). Para os ensaios de tração na flexão na flexão nas 7 e 28 dias os Aditivos 01 e 02 apresentaram as melhores resistências.
Resumen : This paper aims to analyze the lifetime, compatibility, saturation point and the mechanical properties of three polycarboxylate based superplasticisers additives, on Portland cement mixtures. For this study, mixtures with two types of Portland cement (CP IV and CP II E) were prepared and a water/cement ratio of 0.35. The behavior of the samples were analyzed in mixtures containing different additive levels. The levels were related to the solids weight of the additive by weight of cement, ranging from 0.2% to 0.8%. Marsh Funnel and Mini abatimento tests were performed, where through the saturation curve (the point at which the additive fails to provide improvements, and start to decrease the flow) is possible to analyze compatibility and additives saturation point for each type of cement. The mixtures were analyzed at different time control, thirty minutes, one hour, two hours, three and four hours after mixing, in order to determine their useful lifetime (when the additiveis no longer providing plastic improvements to the mixture). The mechanical characteristics were determine by axial compressive and tensile tests for 7 and 28 days. After analysis of the results it is noted that the saturation point for both additives in the mixtures with CP IV was between 0.4% and 0.5%. For the mixtures with cement CP II E the saturation point was between 0.5%and0.6%. The additive 03 showed the best compatibility and lifetim e among the analyzed additives, providing plasticity gains until the last reporting period(four hours after mixing). For the axial compressive strength tests,the additive 03 showed the best results for both time control (7 and 28days). For the tensile tests on 7 and 28 days the additives 01 and 02 showed the best resistance.
Palabras clave : Civil engineering
Lifetime (Engineering)
Resistance
Portland cement
Engenharia civil
Vida útil (Engenharia)
Cimento Portland
CNPQ: CNPQ::ENGENHARIAS
Editorial : Universidade Federal do Pampa
Campus: Campus Alegrete
Tipo de acesso: Attribution-NonCommercial-NoDerivs 3.0 Brazil
Licença: http://creativecommons.org/licenses/by-nc-nd/3.0/br/
URI : http://dspace.unipampa.edu.br/jspui/handle/riu/1691
Fecha de publicación : 4-dic-2015
Aparece en las colecciones: Engenharia Civil



Este ítem está sujeto a una licencia Creative Commons Licencia Creative Commons Creative Commons